Resin-SZUV-W8006-exquisite white
Introduction of 3D Printing Materials
Characteristics
SZUV-W8006??
PRODUCT DESCRIPTION?
SZUV-W8006?is an ABS like SL resin which has accurate and durable features. It is designed for solid state SLA platforms.?SZUV-W8006?can be applied in master patterns, concept models, general parts and functional prototypes in the?field of automotive, medical and consumer electronics industries. The parts durability building with SZUV-W8006?is over 6.5 months.??
TYPICAL FEATURES
-Liquid resin is medium viscosity, so easy for recoating, easy to clean parts and machines?
-Improved strength retained, improved dimensions retention of parts in humid condition?
-Need minimal part finishing
-Long shelf life in machine
?TYPICAL BENEFITS
-Need less part finishing time, easier post-curing
-Building accurate and high tough parts with an improved dimensional stability?
-High quality controls for vacuum casting parts?
-Low shrink and good resistance to yellowing?
-Magnificent white color?
-Outstanding machinable SLA material
?Physical Properties – Liquid Material?
| Appearance | White |
| Density? | 1.13g/cm3?@ 25 ℃ |
| Viscosity? | 376?cps @ 27?℃ |
| Dp? | 0.148?mm |
| Ec? | 7.8?mJ/cm2 |
| Building layer thickness? | 0.1mm |
?Note: the temperature of szuv-w8006 should not be too high. Please use it below 25℃. Recommended temperature for use and preservation is 18-25 ℃.
Handling And Storage
（1） Operation treatment technical measures
?Avoid contact with eyes, skin and clothing. Don't inhaling mist or steam, don't accidentally swallow, keep container tightly closed after the thorough cleaning.
（2） Partial or full ventilation, maintain adequate ventilation
（3） Safe handling matters needing attention???No?smoke, no fire
（4） Safe storage conditions
?Stored in a cool, well-ventilated place, away from heat, sparks and flames. Keep container tightly closed until it is put into use.
（5） packaging container and material
?In the process of custody, please do not transfer to other containers. Don't fall back to the original containers of products that will be used.
Samples
Application Cases
Education
Rapid prototype
Auto Parts
Constructional design
Art Design
Medical
Physical Properties (Liquid)?
| Appearance | White |
| Density? | 1.13g/cm3?@ 25 ℃ |
| Viscosity? | 376?cps @ 27?℃ |
| Dp? | 0.148?mm |
| Ec? | 7.8?mJ/cm2 |
| Building layer thickness? | 0.1mm |
Mechanical Properties (Post-Cured)
| MEASUREMENT | TEST METHOD |
VALUE |
| 90-minute UV post-cure | ||
| Hardness, Shore D | ASTM D 2240 | 87 |
| Flexural modulus, Mpa | ASTM D 790 | 2,592-2,675 |
| Flexural strength, Mpa | ASTM D 790 | 70- 75 |
| Tensile modulus, MPa | ASTM D 638 | 2,599-2,735 |
| Tensile strength, MPa | ASTM D?638 | 39-56 |
| Elongation at break | ASTM D 638 | 13?-20% |
| Poisson’s Ratio | ASTM D 638 | 0.4-0.43 |
| Impact strength notched Izod, J/m | ASTM D 256 | 35?- 45 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 62 |
| Glass transition, Tg，℃ | DMA，E”peak | 73 |
| Coefficient of thermal expansion, /℃ | TMA(T<Tg) | 95*E-6 |
| Density, g/cm3 | ? | 1.16 |
| Dielectric Constant?60 Hz | ASTM D 150-98 | 4.6 |
| Dielectric Constant?1 kHz | ASTM D 150-98 | 3.9 |
| Dielectric Constant?1 MHz | ASTM D 150-98 | 3.6 |
| Dielectric?Strength kV/mm | ASTM D 1549-97a | 14.9 |
Note: the temperature of szuv-w8006 should not be too high. Please use it below 25℃. Recommended temperature for use and preservation is 18-25 ℃.
?